TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar is a martensitic Ti-Al-Mo-Cr-Fe-Si system α+β two-phase thermally strong titanium alloy with good comprehensive properties...
TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar is a martensitic Ti-Al-Mo-Cr-Fe-Si system α+β two-phase thermally strong titanium alloy with good comprehensive properties. Its nominal composition is Ti-6Al-2.5Mo-1.5Cr-0.5 Fe-0.3Si, the α/β transition temperature is between 960 and 1000 °C. In China, a lot of work has been done on the processing technology and performance optimization of TC6 titanium alloy forgings, castings, pipes and rods, etc. TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar, It is a two-phase titanium alloy with complex microstructure. It has the advantages of low density, high strength, corrosion resistance, etc.
Introduction of TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar:
Product model: TC6 (Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si),
State: M (Y/R/ST) hot working state (R), cold working state (Y), annealing state (M)
Titanium rod manufacturing process: hot forging - hot rolling - turning (polishing).
Production standards: There are two implementation standards for titanium plates, the national standard is GB/T3621-2007, GB/T13810-2007, and the American standard is ASTM B265, ASTM F136, ASTM F67, AMS4928.
Surface treatment: bright, polished, pickled, sandblasted, etc.
Common size: thickness Φ (5-400), the indefinite length of the processed bar is 300-6000mm, the indefinite length of the annealed bar is 300-2000mm, the fixed or double length should be within the range of the indefinite length .The allowable deviation of the fixed length is +20mm; the length of the double length should also be included in the incision amount of the bar, and each incision is 5mm. The length of the fixed length or the double length should be indicated in the contract.
(The size is customized according to customer requirements.)
Packing: Export standard wooden box or wooden pallet.
TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar
|
Alloy
|
Element (%) |
Fe |
C |
N |
H |
O |
Cr |
Si |
AL |
Mo
|
Other element |
Ti |
|
|
Each |
Total |
||||||||||||
|
TC6 |
Max |
0.2-0.7 |
0.08 |
0.05 |
0.015 |
0.18 |
0.8-2.3 |
0.15-0.4 |
5.5-7.0 |
2.0-3.0 |
0.10 |
0.40 |
Remain |
TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar Mechanical properties:
|
Alloy
|
Temper
|
Yield Strength Rm/Mpa |
Tensile strength Rp0.2/Mpa |
Elongation rate after break A/% |
rate of reduction in area Z/% |
|
TC6 |
- |
≥980 |
≥840 |
≥10 |
≥25 |
TC6(Ti-6Al-1.5Cr-2.5Mo-0.5Fe-0.3Si) titanium alloy extruded forging rod bar application fields:
In addition to the advantages of high specific strength and good corrosion resistance of ordinary titanium alloys, this alloy also has good comprehensive mechanical properties at room temperature and high temperature, and the operating temperature can be as high as 450 °C. Parts, can also be used to manufacture aircraft bulkheads, joints and other parts.